Abstract

Results of fractographic investigations of effect of electrodynamic treatment on increase of fracture resistance for flat specimens from aluminum alloy AMg6 under cyclic loading were studied. It was shown that conditions of fastening for workable specimen influence substantially on AMg6 alloy resistance to crack nucleation under symmetric loading cycle with amplitude close to proof yield strength of metal.